品名:聚酰胺6或尼龍6(PA6)

LNP™ COLORCOMP™ PX99848 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ FARADEX™ PS003E compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ FARADEX™ PS003E compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ FARADEX™ PS003E compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ KONDUIT™ PTF2BXXX compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ KONDUIT™ PTF2BXXX compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ KONDUIT™ PTF2BXXX compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ KONDUIT™ PX08321 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ KONDUIT™ PX08321 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ KONDUIT™ PX08321 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ KONDUIT™ PX08322 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ KONDUIT™ PX08322 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ KONDUIT™ PX08322 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ KONDUIT™ PX09322 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ KONDUIT™ PX10322 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ KONDUIT™ PX11311 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ KONDUIT™ PX11311 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ KONDUIT™ PX11311U compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ KONDUIT™ PX11313 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ KONDUIT™ PX11313 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ KONDUIT™ PX11422 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ LUBRICOMP™ PFI12R compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ LUBRICOMP™ PFI12R compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ LUBRICOMP™ PFL36 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ LUBRICOMP™ PFL36 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ LUBRICOMP™ PFL38S compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ LUBRICOMP™ PFN16 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ LUBRICOMP™ PFN16 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ LUBRICOMP™ PFP36 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ LUBRICOMP™ PFP36 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ LUBRICOMP™ PI001 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ LUBRICOMP™ PL002 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ LUBRICOMP™ RFN16 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ LUBRICOMP™ RFN16 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ STAT-KON™ PD000 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ STAT-KON™ PE002Z compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ STAT-KON™ PFD04 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ STAT-KON™ PFD04ES compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ STAT-KON™ PFD04S compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ STAT-KON™ PFD06 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ STAT-KON™ PFD06 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ STAT-KON™ PX05047 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ STAT-KON™ PX08024 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ STAT-KON™ PX93058 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ STAT-LOY™ P3000U compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ STAT-LOY™ PF303 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ STAT-LOY™ PF303 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ STAT-LOY™ PF306 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PB006EQ compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PB006SXS compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PC006 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PF001S compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF001S compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF002 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF003 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF003 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF004 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PF004S compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF004S compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF005 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PF005S compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF005S compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF006 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF006S compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF006S compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PF006U compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF006U compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF006U compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PF007 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF008 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF008 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF008QS compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF008S compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF008S compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF009 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF009 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF00A compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF00A compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF00ASXS compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF00ASXS compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF00C compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF00C compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF00C compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PF00CS compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PF1006HI005 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PFB55 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PFB91S compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PFW53U compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PFW53U compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PFW64 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PH0220AC compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PH0240A compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PH0320A compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PH0320A compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PH0400CX_BK1D466 compound | SABIC Innovative Plastics | 尼龍6 |
產(chǎn)品說明 | |
LNP* LUBRICOMP* PL002 is a compound based on Nylon 6 base resin containing 10% PTFE. Added feature of this grade includes: Wear Resistant. Also known as: LNP* Lubricomp* Compound PL-4020 BK8-115 Product Reorder name: PL002 | |
總體 | |
材料狀態(tài) | 已商用:當前有效 |
資料 1 | Technical Datasheet |
搜索 UL 黃卡 | SABIC Innovative PlasticsLNP™ LUBRICOMP™ |
供貨地區(qū) | 北美洲 |
添加劑 | PTFE潤滑劑 (10%) |
性能特點 | 經(jīng)潤滑耐磨損性良好 |
加工方法 | 注射成型 |
物理性能 | 額定值 | 單位制 | 測試方法 |
比重 | 1.19 | g/cm3 | ASTM D792, ISO 1183 |
收縮率 | ASTM D955 | ||
流動: 24小時 | 1.0 到 3.0 | % | |
橫向流動: 24小時 | 1.0 到 3.0 | % |
機械性能 | 額定值 | 單位制 | 測試方法 |
拉伸模量 2 | 3730 | MPa | ASTM D638 |
抗張強度 3 (斷裂) | 52.7 | MPa | ASTM D638 |
伸長率 3 (斷裂) | 25 | % | ASTM D638 |
彎曲模量 4 | 2150 | MPa | ISO 178 |
彎曲強度 | 78.0 | MPa | ISO 178 |
摩擦系數(shù) | ASTM D3702 Modified | ||
與自身 - 動態(tài) | 0.60 | ||
與自身 - 靜態(tài) | 0.42 | ||
磨損因數(shù) | ASTM D3702 Modified | ||
Ring | 0.300 | 10^-10 in^5-min/ft-lb-hr | |
Washer | 74.0 | 10^-10 in^5-min/ft-lb-hr | |
沖擊性能 | 額定值 | 單位制 | 測試方法 |
懸壁梁缺口沖擊強度 | |||
23°C | 48 | J/m | ASTM D256 |
23°C 5 | 4.9 | kJ/m2 | ISO 180/1A |
無缺口懸臂梁沖擊 | |||
23°C | 1200 | J/m | ASTM D4812 |
23°C 5 | 68 | kJ/m2 | ISO 180/1U |
裝有測量儀表的落鏢沖擊 | |||
23°C, Total Energy | 9.60 | J | ASTM D3763 |
-- | 24.7 | J | ISO 6603-2 |
熱性能 | 額定值 | 單位制 | 測試方法 |
熱變形溫度 | |||
0.45 MPa, 未退火, 3.20 mm | 144 | °C | ASTM D648 |
0.45 MPa, 未退火, 64.0 mm 跨距 6 | 133 | °C | ISO 75-2/Bf |
1.8 MPa, 未退火, 3.20 mm | 54.0 | °C | ASTM D648 |
1.8 MPa, 未退火, 64.0 mm 跨距 6 | 51.0 | °C | ISO 75-2/Af |
線形膨脹系數(shù) | ASTM D696 | ||
流動: -30 到 30°C | 0.000096 | cm/cm/°C | |
橫向: -30 到 30°C | 0.000095 | cm/cm/°C |
注射 | 額定值 | 單位制 | |
干燥溫度 | 82.2 | °C | |
干燥時間 | 4.0 | hr | |
建議的zui大水分含量 | 0.15 到 0.25 | % | |
螺筒后部溫度 | 249 到 260 | °C | |
螺筒中部溫度 | 266 到 277 | °C | |
螺筒前部溫度 | 277 到 288 | °C | |
加工(熔體)溫度 | 266 到 277 | °C | |
模具溫度 | 82.2 到 93.3 | °C | |
背壓 | 0.344 到 0.689 | MPa | |
螺桿轉(zhuǎn)速 | 30 到 60 | rpm |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
PA6, 美國液氮, PL002 經(jīng)潤滑 耐磨損性良好其它產(chǎn)品
PA6, 美國液氮, PL002 經(jīng)潤滑 耐磨損性良好
PA6, 美國液氮, PI001 硅酮潤滑劑
PA6, 美國液氮, PFP36 耐磨損性良好PTFE+硅酮潤滑劑
PA6, 美國液氮, PFN16 二硫化鉬潤滑劑
PA6, 美國液氮, PFL38S 經(jīng)潤滑 熱穩(wěn)定性
PA6, 美國液氮, PFL36 PTFE潤滑劑
PA6, 美國液氮, PFI12R 經(jīng)潤滑 耐磨損性良好
PA6, 美國液氮, PX11422 導電 導熱
PA6, 美國液氮, PX11313 導熱 阻燃性能
PA6, 美國液氮, PX11311U 導熱 無溴