品名:聚酰胺6或尼龍6(PA6)

Orgalloy® LE 60ES | Arkema | Nylon 6 Alloy | |
Orgalloy® LE 60HM | Arkema | Nylon 6 Alloy | |
Orgalloy® LE 60LM | Arkema | Nylon 6 Alloy | |
Orgalloy® LE 60LMXV | Arkema | Nylon 6 Alloy | |
Orgalloy® LE 60SF | Arkema | Nylon 6 Alloy | |
Orgalloy® LE 60THM | Arkema | Nylon 6 Alloy | |
Orgalloy® LE 60XV | Arkema | Nylon 6 Alloy | |
Orgalloy® LT 4060 | Arkema | Nylon 6 Alloy | |
Orgalloy® LT 4060ES | Arkema | Nylon 6 Alloy | |
Orgalloy® LT 5050 | Arkema | Nylon 6 Alloy | |
Orgalloy® LT 5050ES | Arkema | Nylon 6 Alloy | |
Orgalloy® R 60ES | Arkema | Nylon 6 Alloy | |
Orgalloy® RS 6000 | Arkema | Nylon 6 Alloy | |
Orgalloy® RS 6010 | Arkema | Nylon 6 Alloy | |
Orgalloy® RS 6030 | Arkema | Nylon 6 Alloy | |
Orgalloy® RS 60E10 | Arkema | Nylon 6 Alloy |


總體 | ||||
材料狀態(tài) |
| |||
搜索 UL 黃卡 |
| |||
供貨地區(qū) |
| |||
添加劑 |
| |||
性能特點 |
| |||
形式 |
| |||
加工方法 |
| |||
多點數(shù)據(jù) |
|
物理性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測試方法 |
密度 | 0.0379 | 0.0379 | lb/in3 | ISO 1183 1 |
熔體體積流動速率 (235°C/2.16 kg) | 0.214 | -- | in3/10min | ISO 1133 1 |
吸水率 | ISO 62 1 | |||
飽和 | 5.5 | -- | % | |
平衡 | 1.5 | -- | % |
機械性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測試方法 |
拉伸模量 | -- | 116000 | psi | ISO 527-2 1 |
拉伸應(yīng)力 (屈服) | -- | 4790 | psi | ISO 527-2 1 |
拉伸應(yīng)變 (屈服) | -- | 7.0 | % | ISO 527-2 1 |
斷裂伸長率 | -- | > 50 | % | ISO 527-2 1 |
熱性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測試方法 |
熔融溫度 2 | 428 | -- | °F | ISO 11357-3 1 |
電氣性能 | 干燥 | 調(diào)節(jié)后的 | 測試方法 | |
漏電起痕指數(shù) | -- | 600 | IEC 60112 1 | |
可燃性 | 干燥 | 調(diào)節(jié)后的 | 測試方法 | |
燃燒性能 正常厚度 1.6mm (0.06 in) | HB | -- | ISO 1210 1 | |
一定厚度與小時下的阻燃等級 (0.126 in) | HB | -- | ISO 1210 1 |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
PA6, 法國阿科瑪, LE 60XV 型材擠出成型 注射成型其它產(chǎn)品
PA6, 法國阿科瑪, LE 60XV 型材擠出成型 注射成型
PA6, 法國阿科瑪, LE 60THM 型材擠出成型 砑光
PA6, 法國阿科瑪, LE 60SF 薄膜擠出 擠出 澆鑄
PA6, 法國阿科瑪, LE 60LMXV 型材擠出成型 注射成型
PA6, 法國阿科瑪, LE 60LM 薄膜擠出 吹塑成型 擠出
PA6, 法國阿科瑪, LE 60HM抗撞擊性,良好 可電鍍
PA6, 法國阿科瑪, LE 60ES 可電鍍 耐熱性,高
PA6, 法國阿科瑪, LE6000
PA6 , 中國臺灣三菱, 1030
PA6 , 中國臺灣三菱, 1020A7